CFC Free One Component PU Foam Chemical Products

They also have advantages in high resilience, low temperature performance and resistance to water attack(hydrolysis). Polyethers also have lower viscosity and specific gravity.

Send Inquiry

Product Introduction

We rely on innovative core technology, industrial devices and efficient operation mode to provide customers with more competitive PU Color Sheet, PU SHEET, PU Square Pad. attitude determines everything; details makes success. Attitude determines behavior, behavior develops character, and character determines destiny. Customers' gratification is our greatest advertising.

Polyether based Casting Polyurethane prepolymer

1.Polyether based polyurethane prepolymer are recommended for applications where parts undergo dynamic stress, etc, they incur lower heat build-up. They also have advantages in high resilience, low temperature performance and resistance to water attack(hydrolysis). Polyethers also have lower viscosity and specific gravity.

2. Specifications,Application and operation details

PPG/TDI system Casting Polyurethane prepolymer

Item	Type
Item	HJ-1880	HJ-1885	HJ-1890	HJ-1895
NCO% Content	3.7±0.2	4.0±0.2	5.0±0.2	6.2±0.2
Density 25℃/(g/cm³)	1.10	1.10	1.10	1.10
Viscosity 80℃/mpa·s	500-700	500-700	400-600	150-200
Appearance at 25℃	Colorless transparent liquid
Mix Temperature ℃ Prepolymer /Moca	80℃/115℃	80℃/115℃	75℃/115℃	75℃/115℃
Gel Time /min	8-12	6-8	3-5	2-4
Vulcanization Time (h)	25-16	25-16	25-16	25-16
Physical Properties
Hardness (Shore A)	80±2	85±2	90±2	95±2
Tensile Strength (Mpa)	12-15	14-18	20-24	22-26
100% Modulus (Mpa)	7-8	8-9	10-11	11-12
300% Modulus (Mpa)	--	11-12	16-17	20-21
Elongation at Break (%)	260-320	300-400	340-420	350-420
Tear Strength (KN/m)	50-55	65-75	80-90	85-95
Compression permanent deformation %	6-8	6-8	4-6	4-6
DIN Abrasion loss（mm³）	≤160	≤150	≤140	≤130
Resilience %/25℃	20-24	19-22	18-20	16-18
- Product application: Rod and bar, sheet and plate, seal, drag roller, caster, grinder lining, pipe lining, miscellaneous parts and other products. - Operation details: After vacuum degasing at 75-85 ℃, the prepolymer is mixed with melted MOCA for casting and vulcanization. It is suitable for manual and mechanical operation. - Storage: Store in a cool and dry place and use up as soon as possible after opening; If it cannot be used up at one time, it shall be sealed with nitrogen; The second opening needs to be used for defoaming, and the original storage period is six months. - Packing: 20kg or 200kg iron drum

Our company's CFC Free One Component PU Foam Chemical Products are produced in batches to ensure that the products are cheap and high quality. In the fierce market competition, the company adheres to the spirit of "innovative and pragmatic" to make products increasingly mature and perfect. Customers are the support of our business growth, and the enterprise is the trustworthy partner of customers.

Hot Tags: polyether based casting polyurethane prepolymer, China, manufacturers, factory, buy, PTMEG Based Casting Polyurethane Prepolymer, 3 Crystal Water Zinc Borate, MDI Two Componment Polyester Type Casting PU, Two Componment MDI Based Polyurethane Prepolyer, Polyether Based Casting Polyurethane Prepolymer, Zinc Borate 2335 200

[[ProKeywords]]

No Information

Industrial Parts Used Casting Ptmeg+Tdi PU Prepolymer Material