Crosslinking Agent Trimethyleneglycol Di (p-aminobenzoate)
Under conventional hardness, TDI and MDI products have no great difference in strength index, but will have obvious improvement in elasticity and wear resistance.
Product Introduction
We take scientific and technological progress as the prerequisite, keep pace with the times, and strive to build our own well-known Two Componment MDI Based Polyurethane Prepolyer, PU RUBBER SHEET, Hot Casting Polyurethane Prepolyer brand, so as to improve our market competitiveness. We aim at the win-win situation of economic and social benefits, and pursue to make the enterprise stronger, bigger and better. With the new management mode, perfect technology, thoughtful service and perfect quality as the survival basis, we always insist on the customer first and heart to serve the customers, and insist on using their own services to move customers.
Characteristics of MDI raw materials
1. Under conventional hardness, TDI and MDI products have no great difference in strength index, but will have obvious improvement in elasticity and wear resistance.
MDI products will have better wear life and softer hand feeling.
Indicators | Polyester TDI | Polyester MDI |
Hardness (shA) | 90 | 90 |
Tensile strength (Mpa) | 51 | 48 |
Elongation (%) | 577 | 546 |
Tear strength (KN/m) | 107 | 102 |
Rebound (%) | 30 | 40 |
Wear (mm3) | 50 | 38 |
2.Fast reaction rate
With high NCO content and catalyst intervention, the reaction rate of MDI feedstock is 1-2 times faster than that of TDI series feedstock.
3.Environmental protection
The vapor pressure of MDI is much lower than that of TDI, and it has aromatic odor and little toxicity in the production process, so MDI is a new material that meets the needs of environmental protection
4.Low application temperature of materials
Because of the high activity of MDI, the application temperature of MDI raw materials is much lower than that of TDI series raw materials in order to prevent the degradation of physical properties of final products caused by self-polymerization of raw material.
5. Because of the high resilience and flexibility, MDI series products are much better than TDI series products in the application effect of sieve plate. The improvement of elasticity is helpful to improve the impact wear resistance and self-cleaning effect of products.
Type | HJ2285M | HJ2290M | HJ2295M | HJ2385M | HJ2390M | HJ2395M |
NCO content /% | 6.0±0.2 | 7.5±0.2 | 8.8±0.2 | 6.0±0.2 | 7.5±0.2 | 8.8±0.2 |
Appearance in 20℃ | PTMEG type，white solid | Polyester type，white solid | ||||
1,4-BD dosage (100gPUP )/g | 6.2 | 7.7 | 9.1 | 6.2 | 7.7 | 9.1 |
Viscosity(85℃)/mPa·s | 1300-1500 | 900-1100 | 750-850 | 1300-1500 | 1100-1300 | 900-1100 |
Mixing temperature/℃ （PUP/1,4BD） | 85/40 | 85/40 | 80/40 | 85/40 | 85/40 | 80/40 |
Catalyst addition dosage (1000gPUP)/g | Catalyst addition dosage (1000gPUP)/g | |||||
Gel time /min | 8—10 | 5—7 | 4—6 | 8—10 | 5—7 | 4—6 |
Vulcanization Time (100-110℃)/h | 24-48 | 24-48 | 24-48 | 24-48 | 24-48 | 24-48 |
Hardness（shore A） | 85±2 | 90±2 | 95±2 | 85±2 | 90±2 | 95±2 |
Tensile strength/MPa | 34-39 | 37-42 | 43-48 | 42-47 | 48-53 | 52-57 |
100% Modulus /MPa | 4—6 | 5—8 | 10—14 | 3—6 | 8—10 | 10—13 |
300%Modulus /MPa | 10—15 | 13—18 | 20—30 | 8—14 | 16—20 | 20—24 |
Elongation at break/ % | 360-460 | 560-660 | 440-540 | 530-630 | 580-680 | 480-580 |
Tear strength（KN/m） | 60-70 | 95-105 | 105-115 | 75-85 | 105-115 | 115-125 |
Rebound/ % | 48-50 | 46-48 | 45-47 | 45-47 | 42-45 | 40-43 |
Specific gravity（25℃）（g/ cm3） | 1.11 | 1.11 | 1.12 | 1.23 | 1.23 | 1.24 |
DIN Abrasion loss /mm³ | ≤38 | ≤35 | ≤32 | ≤38 | ≤38 | ≤36 |
We are a professional enterprise engaged in the development, manufacture, production and sales of Crosslinking Agent Trimethyleneglycol Di (p-aminobenzoate). We take pride in achieving and maintaining consistency high standards of quality. Please feel free to contact us! We encourage employees to actively participate in annual outdoor training to enhance corporate team cohesiveness. Integrity is the minimum moral requirement of the company for employees to deal with the world.
Hot Tags: two componment mdi based polyurethane prepolyer, China, manufacturers, factory, buy, Quazi MDI Three Componment Casting PU, PU Tube and Pipe, 7 Crystal Water Zinc Borate, PTMEG Type MDI System Polyurethane Elastomer, PTMEG Based Casting Polyurethane Prepolymer, Polyether Based Casting Polyurethane Prepolymer